T-butyl cascade polymers

ABSTRACT

A method for forming cascade polymers specifically utilizing the amine monomer of the formula  
                 
 
     The monomer is made by initially reacting nitromethane and CH 2 ═CHCO 2 -TBu by nucleophilic addition to form the triester nitrotrialkanoate of the formula  
                 
and then reducing the nitrosubstituent to afford the said amine monomer.

TECHNICAL FIELD

The present invention relates to the field of polymer chemistry and, more specifically with regard to the field of cascade or dendritic polymer chemistry. These polymers are based upon the application of mathematical progressions to organic synthesis and thereby possess well-defined molecular topologies.

BACKGROUND OF THE INVENTION

The field of cascade polymer chemistry is expanding the traditional synthetic limits into the meso-macro-molecular frontier. Such polymers possess well-defined molecular topologies as they can be constructed in discrete layers rendering upon the molecule discrete, symmetric and consistent chemical characteristics.

These polymeric structures provide specific micellar molecules.

The synthesis and spectral features of cascade polymers, also referred to as arborols possessing two-, three- and four-directional microenvironments with functionalized polar outer surfaces, have been recently reported (1-8). Depending on their molecular shape, many of these macromolecules aggregate to form gels or show novel micellar characteristics in aqueous solution (3,7,8). In view of an interest in generating a spherical hydrophilic surface with a compact lipophilic core, the present invention provides a cascade system which in one embodiment emanates from a central adamantane core. This core includes bridgehead positions which have suitable geometry to mimic a tetrahedral nucleus and can be envisioned as an extended methane core. Such a core is an ideal starting point toward four-directional cascade polymers.

In constructing such spherical polymers, several further problems were uncovered. One such problem related to the generation of a tri-branched monomer which would not cyclize. More specifically, to provide tri-valent branching from a single branch of a polymer, at least two qualities are required. First, there must be directionality such that the monomer combines with the branch so as to expose three branch binding sites for further tiering of the macromolecule. The branches of the macromolecule extending from a central core must also extend sufficiently to be able to allow further reactions therewith for the additional tiering while not cyclizing onto themselves. Cyclizing removes branches from being chemically reactive thereby causing a dead-end to the tiering process. For example, the following reaction sequence generated the polymeric product set forth below.

Attempted oxidation of compound 11 by a RuO₂ procedure of Irngartinger, et al. (9) resulted in limited success in that complete oxidation was not reproducible.

Applicant herein provides novel monomers which are ideal in that they do not cyclize and further can be used in a cascade system for producing macromolecular monomers through tetradirectional polymers, particularly on an adamantane, methane equivalent, or four-directional core.

Further, the present invention provides novel four-directional spherical dendritic macromolecules based on adamantane made in accordance with the novel method set forth herein.

SUMMARY OF THE INVENTION

In accordance with the present invention, there is a method forming an amine monomer of the formula

by the steps of reacting nitromethane and CH₂═CHCO₂-TBu by nucleophilic addition to form the triester nitrotrialkanoate of the formula

and reducing the nitrosubstituent to said amine monomer.

Further in accordance with the present invention the novel amine monomer can be used to create several novel one, two, three, or four-directional polymers based on the adamantane, or similar core.

DETAILED DESCRIPTION OF THE INVENTION

The present invention generally will provide a monomer of the formula

wherein R is selected from the group consisting essentially of NH₂ and NO₂. This novel compound is a building block for novel cascade polymers made in accordance with the inventive method set forth below. Products made in accordance with the present invention can be used in various fields, such as pharmaceutical chemistry, as micelles. However these compounds are used to make unimolecular micelles as opposed to multi-molecular micelles, previously known in the art.

These monomeric micelles generally have a core and branching which leads from the core. In accordance with the present invention, the branching can be tetra-directional extending from the four bridgehead positions of the core and can be tiered or layered such that a first layer of branching can be combined with the core and then subsequent layers can be added to provide a well-defined molecular topology.

More specifically, as discussed above, attempted oxidation of the arborol of the formula

by the RuO₂ procedure discussed above met with limited success in that complete oxidation was not reproducible. To circumvent this problem as well as to shorten the overall iterative procedure, the novel building block di-tert-butyl 4-amino-[2-(tert-butoxycarbonylethyl]-heptanedioate was prepared by the following scheme.

A key factor was the bulky nature of the tert-butyl ester, so it was necessary to prevent lactam formation during reduction of the nitro functionality. That is, the following reaction did not occur under the condition conducted in accordance with the present invention.

An attempt to synthesize the nitro ester precursor by modification of the procedure reported by Bruson and Riener(10) using tert-butyl acrylate in place of the acrylonitrile resulted in a poor yield of about 5%. To circumvent this sluggish nucleophilic addition, the reaction temperature was elevated during the initial addition phase and then maintained at about 70° to 80° C. for one hour. This modification resulted in a 72% yield of the desired triester, which was confirmed by ¹³C NMR by the peaks for the quaternary and carbonyl carbons at 92.1 and 170.9 ppm, respectively. The ¹H NMR spectrum showed a singlet at 1.45 ppm assigned to (CH₃)₃CO in a multiplet at 2.21 ppm for the methylene protons. Analysis of the crystal structure ultimately confirmed the analysis.

The prior art discusses diverse reduction conditions for the conversion of nitroalkanols to aminoalkanols(11). The use of platinum, palladium, or Raney nickel catalyst all resulted in very poor yields and gave mostly recovered nitrotrialkanoate compound. However, a reduction with specially generated T-1 Raney nickel by the process of Domingues, et al. (12) at elevated temperatures (ca. 60° C.) gave an 88% yield of the aminoester after purification. Successful reduction was confirmed by ¹³C NMR by an upfield shift for the quaternary carbon at 52.2 ppm. The ¹H NMR spectrum of the aminotrialkanoate showed a singlet at 1.44 ppm for the tert-butyl group, multiplets at 1.68 and 2.26 ppm for the methylene protons and a broad singlet at 5.49 ppm for the amino moiety.

Since related alkyl esters of the aminotrialkanoate could not be prepared because of facile intramolecular lactam formation during the hydrogenation of the nitro moiety, the tert-butyl ester is ideal in that no cyclization was observed. The advantages of the tert-butyl ester are: a) reduced number of overall steps for cascade synthesis; b) easy preparation on a large scale; c) facile hydrolysis to the desired acids in nearly quantitative yield; and d) the poly tert-butyl esters were easily purifiable solids.

An example of the use of the tert-butyl ester in a cascade synthesis is as follows. Treatment of adamantanecarbonyl chloride with the aminotrialkanoate as set forth above furnished 71% yield of the desired triester (amine monomer) of the formula

This structure was confirmed by ¹³C NMR by the peaks at 172.8 (ester), 177.4 (CONH), and 56.7 ppm (side-quaternary carbon). Hydrolysis of the ester to a triacid was accomplished with about 100% yield by treatment with formic acid. It was identical in all respects to a sample prepared by the above procedure. Application of peptide coupling procedures known in the art of the acid with the aminotrialkanoate in the presence of DCC and 1-hydroxybenzotriazole in dry dimethyl formamide (DMF) afforded a 61% yield of a nonaester(13). The following scheme summarizes the reaction sequence

The presence of the structure was confirmed by ¹³C NMR showing two carbonyl peaks at 172.6 (ester) and 177.0 ppm (CONH) as well as the peaks for the side-chain quaternary carbons at 57.6 and 57.0 ppm thereby confirming the transformation. The specific assignment of internal and external methylene signals was based on the intensity ratios as well as the fine shape, the internal methylenes being broader. The final acid was obtained in a 95% yield by the treatment of the ester with formic acid. The absence of the tert-butyl groups in the NMR spectra and the shift for the carbonyl, 172.6 ppm (ester) to 177.6 ppm (acid) supports the conclusion that hydrolysis occurred.

A large scale preparation of the nitrotriester and its subsequent reduction to the amine has been developed. Specifically, the nitrotriester 1 was prepared via treatment of nitromethane with slightly more than three equivalents of tert-butyl acrylate in dimethoxyethane (DME). Trace yellow impurities produced in the reaction were easily removed by recrystallization. Removal of these colored contaminants circumvents chromatographic purification of the desired monomer 2.

Hydrogenation of the nitrotriester 1 to the aminotriester 2 at slightly elevated temperature presented a serendipitous exception to the reduction products of known tertiary, γ-nitroester (Weis et al., 1995). All previously known examples of such reductions readily cyclize to afford the corresponding 2,2′-disubstituted pyrrolidones. Therefore, catalytic hydrogenation conducted under carefully controlled temperature conditions using freshly prepared T-1 Raney Nickel at 45-55° C. provided (ca. 90%) the pure monomer 2.

The crystalline amine 2 is stable for prolonged periods when stored at ≦15° C., however the presence of solvent or extended storage at 25° C. can result in the formation (about 5-7% over several months) of di-tert-butyl 5-oxo-2,2-pyrrolidinedipropionate (3) (Young, 1993). Attempts to recrystallize 2 were initially frustrated by the thermal cyclization at elevated temperatures, which further dictated that in vacuo solvent removal be performed below 50° C. Subsequently, it has been determined that aminoester 2 can be cyclized quantitatively in the solid state at 105-110° C.; while in solution, cyclization occurs at 65-80° C.

Experimental Section

General Comments. Melting point data were obtained in capillary tubes with a Gallenkamp melting point apparatus and are uncorrected. ¹H and ¹³C NMR spectra were obtained in CHCl³, except where noted, with Me₄Si as the internal standard (δ=0 ppm), and recorded at either 80 or 360 MHz. Infrared spectral data were obtained on an IBM −38 spectrometer. Elemental analyses were performed by MicAnal Laboratories in Tucson, Ariz.

Di-tert-butyl 4-Nitro-4-[2-tertbutoxycarbonyl)ethyl]heptanedioate. A stirred solution of MeNO₂ (6.1 g, 100 mmol), Triton B (benzyltrimethylammonium hydroxide, 50% in MeOH; heated to 65° to 70° C. tert-Butyl acrylate (39.7 g, 310 mmol) was added portion wise to maintain the temperature at 70° to 80° C. Additional Titon B (2×1 mL) was added when the temperature started to decrease; when the addition was completed, the mixture was maintained at 70° to 75° C. for one hour. After concentration in vacuo, the residue was dissolved in CHCl₃ (200 mL), washed with 10% aqueous HCl (50 mL) and brine (3×50 mL), and dried MgSO₄). Removal of solvent in vacuo gave a pale yellow solid, which was crystallized (95% EtOH) to solid, which was crystallized (95% EtOH) to afford a 72% yield of the triester, as white microcrystals: 33 g; mp 98-100° C.; ¹H NMR δ 1.45 (s, CH₃, 27 H), 2.21 (m, CH₂, 12 H); ¹³C NMR δ 27.9 (CH₃, 29.7 CH₂CO), 30.2 (CCH₂), 80.9 CCH₃), 92.1 (O₂NC), 170.9 (CO); IR (KBr) 1542 (NO₂), 1740 (CO) cm⁻¹. Anal. Calcd for C₂₂H₃₉O⁸N: C, 59.35; H, 8.76; N, 3.14. Found C, 59.27; H, 9.00; N, 3.14.

Di-tert-butyl 4-Amino-4-[2-(tert-butoxycarbonyl)ethyl]heptanedioate. A solution of the above synthesized nitro triester (4.46 g, 10 mmol) in absolute EtOH (100 mL) with T-1 Raney Ni₁₂ (4.0 g) was hydrogenated at 50 psi and 60° C. for 24 hours. The catalyst was cautiously filtered through Celite. The solvent was removed in vacuo, affording a viscous liquid, which was column chromatographed (SiO₂), eluting with EtOAc to give a 88% yield of the amino triester as a white crystalline solid: 3.7 g; mp 50-52° C.; ¹H NMR δ 1.44 (s, CH₃, 27 H), 1.78 (m, CH₂, 12 H); ¹³C NMR δ 27.8 (CH₃), 29.8 (CH₂CO), 34.2 (CCH₂), 52.2 (H₂NC), 80.0 (CCH₃), 172.8 (CO); IR (KBr) 1745 (CO) cm⁻¹. Anal. Calcd for C₂₂H₄₁O₆N: C, 63.58; H, 9.95; N, 3.37. Found C, 63.72; H, 10.05; N, 3.38.

1-[[N-[3-(tert-Butoxycarbonyl)-1,1-bis[2-tertbutoxycarbonyl)ethyl]propyl]amino]carbonyl]adamantane. A solution of 1-adamantanecarbonyl chloride (1 g, 5 mmol), amine monomer (2.1 g, 5 mmol), and Et₃N (600 mg, 6 mmol) in dry benzene (25 mL) was stirred at 25° C. for 20 hours. The mixture was washed sequentially with aqueous NaHCO₃ (10%), water, cold aqueous HCl (10%), and brine. The organic layer was dried (Na₂SO₄) and then concentrated in vacuo to give residue which was chromatographed (SiO₂), eluting first with CH₂Cl₂ to remove some by-products and then with EtOAc to give a 71% yield of the ester as a white solid: 2 g; mp 84-86° C.; ¹H NMR δ 1.46 (s, CH₃, 27 H), 1.68-2.1 (m, CH, CH₂, 27 H), 4.98 (bs, NH, 1 H); ¹³C NMR δ 28.0 (CH₃), 28.2 (γ-CH), 29.8, 30.1 (NHCCH₂CH₂CO), 36.4 (δ-CH₂), 39.2 (β-CH₂), 41.2 (α-C), 56.7 (NHC), 80.5 (CCH₃), 172.8 (COO), 177.4 (CONH); IR (KBr) 3350, 2934, 2846, 1740, 1638, 1255, 1038 cm⁻¹, Anal. Calcd for C₃₃H₅₅O₇N: C, 68.58; H, 9.60; N, 2.43. Found: C, 68.36; H, 9.66; N, 2.36.

1-[[N-]3-[[N-[3-(tert-Butoxycarbonyl)-1,1-bis[2-(tert-butoxycarbonyl)ethyl]propyl]-amino]carbonyl]-1,1-bis[2-[[N-[3-(tert-buxtoxycarbonyl)-1,1-bis[2-(tert-buxtoxycarbonyl)-ethyl]propyl]amino]carbonyl]ethyl]propyl]amino]carbonyl]adamatane. A mixture of the triacid 1-[[N-[3-carboxyl-1,1-bix(2-carboxyethyl)propyl]-amino]carbonyl]adamantane (400 mg, 1 mmol) amine monomer (1.45 g, 3.5 mmol), DCC (620 mg, 3 mmol), and 1-hydroxybenzotriazole (400 mg, 3 mmol) in dry DMF (15 ml) was stirred at 25° C. for 48 hours. After filtration of the dicyclohexylurea, the solvent was removed in vacuo. The residue was dissolved in CH₂Cl₂ (50 mL) and sequentially washed with cold aqueous HCl (10%), water, aqueous NaHCO₃ (10%), and brine. The organic phase was dried (Na₂SO₄). Removal of solvent in vacuo gave a thick viscous residue, which was flash chromatographed (SiO₂) eluting first with EtOAc/CH₂Cl₂ (1:1) then with 5% MeOH in EtOAc, furnished A 61% yield of the ester, as a white solid: 970 mg; mp 115-118° C.; ¹H NMR δ 1.42 (s, CH₃, 81 H), 1.64-2.20 (m, CH, CH₂, 63 H), 5.58 (bs, NH, 4H) ¹³C NMR δ 27.9 (CH₃), 28.4 (γ-CH), 29.6, 30.0 (NHCCH₂CH₂COO), 31.6, 32.2 (NHCCH₂CH₂CONH), 36.6 (γ-CH₂), 39.2 (β-CH₂), 41.1 (α-C), 57.0 (NHCCH₂CH₂COO), 57.6 (NHCCH₂CH₂CONH), 80.3 CCH₃), 172.6 (COO), 177.0 (CONH); IR (KBr) 3348, 2936, 2850, 1740, 1665, 1260, 1040 cm⁻¹. Anal. Calcd for C₈₇H₁₄₈O₂₂N₄: C, 65.22; H, 9.31; N, 3.50. Found: C, 65.41; H, 9.30; N, 3.39.

1-[[N-[3-[[N-[3-Carboxy-1,1-bis(2-carboxyethyl)propyl]amino]carbonyl]-1,1-bix[2-[[N-[3-carboxy-1,1-bix(2-carboxyethyl)propyl]-amino]carbonyl]ethyl]propyl]amino]carbonyl]-adamantane. A solution of the above tert-butyl ester (800 mg, 500 μmol) in formic acid (96%, 5 mL) was stirred at 25° C. for 12 hours. The solvent was removed in vacuo to give a residue; toluene (5 mL) was added and the solution was again evaporated in vacuo to azeotropically remove residual traces of formic acid. The resulting white solid was extracted with warm acetone (5×50 mL). The combined extract was filtered (SiO₂), eluting with acetone. The residue obtained after concentration was dissolved in aqueous NaOH (10%) and acidified with concentration HCl to give 95% yield of the acid as a white solid: 520 mg, mp 346° C. dec; ¹H NMR (Me₂SO-d₆) δ 1.82-2.40 (m, CH, CH₂, 63 H), 4.45 (bs, OH, 9 H, exchanged with D₂O), 6.28 (bs, NH, 4H); ¹³C NMR (Me₂SO-d₆) δ 29.6 (γ-CH), 30.2 (NHCCH₂CH₂COOH), 31.0, 32.4 (NHCCH₂CH₂CONH), 37.8 (δ-CH₂), 40.1 (β-CH₂), 42.5 (α-C), 58.0 (NHCCH₂CH₂CONH), 58.4 (NHCCH₂CH₂COOH), 177.6 (COOH), 179.8 (CONH); IR (KBr) 3360, 3340-2600, 2900, 1744, 1690, 1245, 1090 cm⁻¹. Anal. Calcd for C₅₁H₇₆O₂₂N₄: C, 55.83; H, 6.98; N, 5.11. Found: C, 55.71; H, 7.04; N, 4.98.

The monomers of the present invention can be used for the design and synthesis of novel dendritic polymers which are one, two, three, or four-directional. In accordance with the present invention, the monomers can be used to synthesize four-directional spherical dendritic macromolecules based on adamantane. The use of the aminotrialkanoate monomer offers several advantages. The t-butyl ester intermediates are easily purified solids. Further, only two steps are required to progress from generation to generation.

A specific example of a synthesis is as follows. An acid chloride of the following formula

is treated with the aminotrialkanoatee present invention to afford a dodecaester of the following formula

wherein R=t-Bu.

The dodecaester was hydrolyzed in good yield with 96% formic acid to yield the corresponding dodecaacid.

Addition of further tiers was easily obtained by the coupling of the dodecaacid and further layers of the aminotrialkanoate with DCC an 1-HBT to afford the ester wherein R=TBU. Upon hydrolysis, the ester quantitatively generated the corresponding next tiered polyacid.

A specific example of the method of forming the above-mentioned acid moiety is as follows.

1,3,5,7-Tetrakis{[N-[3-(tert-butoxycarbonyl)-1,1-bis[2-(tert-butoxycarbonyl)ethyl]propyl]amino]carbonyl}-adamantane. A mixture of adamantanetetra-carboxylic acid (78 mg, 250 μmol) and freshly distilled SOCl₂ (2 mL) was refluxed for 4 hours. Excess of SOCl₂ was removed in vacuo, benzene (5 mL) was added, and the solution was concentrated in vacuo to yield the corresponding tetraacyl chloride, as a white solid.

Crude 1,3,5,7-Tetrakis(chlorocarbonyl) adamantane, amine monomer (450 mg, 1.1 mmol), and Et₃N (110 mg, 1.1 mmol) in dry benzene (10 mL) were stirred at 25° C. for 20 hours. Additional benzene (40 mL) was added, and the mixture was sequentially washed with aqueous NaHCO₃ (10%), water, cold aqueous HCl (10%), and brine. The organic phase was dried (Na₂SO₄) and then concentrated in vacuo to furnish a viscous oil, which was chromatographed (SiO₂), eluting with 5% MeOH in EtOAc to generate a 61% yield of the dodecaester, as a white solid: 290 mg; mp 105-107° C.; ¹H NMR δ 1.40 (s, CH₃, 108 H), 172 (s, CH₂, 12 H), 2.24 (m, CH₂, 48 H), 5.88 (bs, NH 4 H); ¹³C NMR δ 28.1 (CH₃), 30.0, 30.4 (CCH₂CH₂COO), 39.0 (β-CH₂), 42.8 (α-C), 57.1 (HNC), 80.2 (CCH₃), 173.1 (COO), 177.6 (CONH); IR (KBr) 3348, 2930, 2845, 1740, 1645, 1260, 1038 cm⁻¹. Anal. Calcd for C₁₀₂H₁₇₂O₂₈N₄: C, 64.38; H, 9.12; N, 2.95. Found: C, 64.52; H, 8.91; N, 2.86.

1,3,5,7-Tetrakis{[N-[3-carboxy-1,1-bis(2-carboxyethyl)propyl]amino]carbonyl}-adamantane. A solution of the dodecaester (190 mg, 100 μmol) in formic acid (96%, 2 mL) was stirred at 25° C. for 20 hours. Excess solvent was removed in vacuo, and toluene (3×2 mL) was added. The solvents were removed in vacuo to give a 94% yield of the dodecaacid, as a white solid: 115 mg; mp 282-284° C. dec; ¹H NMR (D₂O) δ 1.84 (s, CH₂, 12H), 2.34 (m, CH₂, 48H); ¹³C NMR (D₂O) δ 30.1 (CCH₂CH₂COOH), 38.8 (β-CH₂), 42.7 (α-C), 58.6 (HNC), 177.8 (COOH), 180.4 (CONH); (KBr) 3360, 3330-2600, 2903, 1745, 1690, 1245, 1090 cm⁻¹. Anal. Calcd for C₅₄H₇₆O₂₈N₄: C, 52.75; H, 6.23; N, 4.56. Found: C, 52.59; H, 6.22; N, 4.51.

1,3,5,7-Tetrakis{[N-[3-[[N-[3-(tert-butoxycarbonyl)-1,1-bis[2-(tert-butoxycarbonyl)-ethyl]propyl]amino]carbonyl]-1,1-bis[2-[[N-[3-(tert-butoxycarbonyl)-1,1-bis[2-(tert-butoxycarbonyl)ethyl]propyl]amino]carbonyl]-ethyl]propyl]amino]carbonyl}adamantane. A mixture of the dodecaacid (74 mg, 60 μmol), the amine monomer (330 mg, 790 μmol), dicyclohexyl-carbodiimide (DCC; 150 mg, 720 μmol), and 1-hydroxybenzotriazole (100 mg, 740 μmol) in dry DMF (3 mL) was stirred at 25° C. for 48 hours. After filtration of dicyclohexylurea, the solvent was removed in vacuo to give a residue, which was dissolved in EtOAc (25 mL) and was sequentially washed with cold aqueous HCl (10%), water, aqueous NaHCO₃ (10%), and brine. The organic phase was dried (Na₂SO₄) and concentrated in vacuo, and the residue was chromatographed (SiO₂), eluting first with EtOAc/CH₂Cl₂ (1:1) to remove some impurities and then with 5% MeOH in EtOAc to furnish a 58% yield of the ester, as a white solid: 200 mg; mp 138° C.; ¹H NMR δ 1.40 (s, CH₃); ¹³C NMR δ 28.1 (CH₃), 30.0 (CCH₂CH₂CONH), 29.8, 30.2 (CCH₂CH₂COO), 38.9 (β-CH₂), 42.4 (α-C), 57.2 (CCH₂CH₂COO), 57.6 (CCH₂CH₂CONH), 80.0 (CCH₃), 172.8 (COO), 177.8 (CONH); IR (KBr) 3350, 2938, 2846, 1740, 1680, 1260, 1045 cm⁻¹. Anal. Calcd for C₃₁₈H₅₄₄O₈₈N₁₆: C, 63.64; H, 9.14; N, 3.74. Found: C, 63.28; H, 8.96; N, 3.77.

1,3,5,7-Tetrakis{[N-[3-[[N-[3-carboxy-1,1-bis(2-carboxyethyl)propyl]amino]carbonyl]-1,1-bis[2-[[N-[3-carboxy-1,1-bis(2-carboxyethyl)-propyl]amino]carbonyl]ethyl]propyl]amino]-carbonyl}adamantane. A solution of the ester (150 mg, 25 μmol) in formic acid (96%, 2 mL) was stirred at 25° C. for 20 hours. Workup and purification, similar to that of the dodecaacid, gave (95%) the corresponding acid, as a very hygroscopic solid: mp 350-354° C. dec; ¹H NMR (D₂O) δ 1.80 (s, CH₂, 12 H), 2.18-2.41 (m, CH₂, 192 H) ¹³C NMR (D₂O) δ 30.2 (CCH₂CH₂COOH), 30.8, 31.6 (CCH₂CH₂CONH), 39.1 (β-CH₂), 42.8 (α-C), 58.1 (CCH₂CH₂CONH), 58.5 (CCH₂CH₂COOH), 178.0 (COOH), 180.2 (CONH); IR (KBr) 3360, 3340-2600, 2920, 1745, 1685, 1240, 1060 cm⁻¹.

Large Scale Preparation of Di-tert-butyl 4-[2-(tert-butoxycarbonyl)ethyl]-4-nitroheptane-dicarboxylate (1). A 5-liter 3-necked flask, equipped with a 500 mL addition funnel, a thermometer, a reflux condenser and a 2-inch magnetic stirring bar was charged with 1,2-dimethoxyethane (DME, 500 mL) and MeNO₂ (122 g, 108.3 mL, 2 mol). The solution was heated to 65-70° C., and Triton-B (20 mL, 40% in MeOH) was added. Tert-butyl acrylate (794 g, 908 mL, 6.20 mol) was added at such a rate to maintain a temperature of 75-85° C. The addition was completed within 2 to 2.5 hours. When the temperature was maintained at 70-80° C. for two hours, the solution was decanted from insoluble polymeric material (which adheres to the wall of the flask) and concentrated in vacuo. The resulting light yellow residue was dissolved in ether (2.5 L), washed with ice cold 10% aqueous HCl (2×200 mL), an aqueous saturated NaHCO₃ (2×200 mL), and water (2×200 mL), then dried and clarified [Na₂SO₄ (100 g) with celite (10 g)]. The ether was removed in vacuo to give a solid mass, which was dissolved in warm ethanol (ca. 1.3 L). The solution was allowed to cool and maintained at 0° C. for 24 hours. The resultant colorless crystals, were collected, washed with precooled methanol (500-600 mL) to remove any residual colored impurities, and dried in vacuo to afford 668-721 g (75-81%) of the white crystalline 1; mp 99-100° C., lit (Newkome et al., 1991) mp 98-100° C. ¹H NMR: δ 1.45 (s, CH₃, 27H), 2.21 (m, CH₃, 27H), 2.21 (m, CH₂, 12H); ¹³C NMR: δ 27.9 (CH₃), 29.7 (CH₂CO), 30.2 (CCH₂), 80.9 (CCH₃), 92.1 (CNO₂), 170.9 (CO₂).

Di-tert-butyl 4-[2[(tert-butoxycarbonyl)ethyl]-4-aminoheptanedicarboxylate (2)

A. Preparation of T-1 Raney Nickel Catalyst (Dominguez et al., 1961). Caution should be maintained as this catalyst is easily handled when wet; however, it is extremely pyrophoric when dried and exposed to air. To 705 mL of water in a 2 L beaker rapidly stirred using a 2-inch magnetic stirring bar was added NaOH pellets (75 g). After dissolution, aluminum nickel alloy [30 g, Aldrich Chemical Co. (22,165-1), Raney R-type alloy] was added in one portion to the hot solution. There was a vigorous evolution of hydrogen and the temperature rose to ca. 85-90° C.; stirring was continued for one hour. The beaker was covered with a watch glass, and the supernatant alkaline solution was carefully decanted from the black catalyst. Distilled water (300-400 mL) was added, stirred for one to two minutes, and then decanted. This procedure was repeated four times. The catalyst was transferred into a 250 mL beaker and washed with absolute ethanol (5×150-200 mL); each time the catalyst was allowed to settle before the supernatant ethanol was decanted. The moist catalyst was used immediately.

B. Reduction Procedure. To a Parr hydrogenation bottle was added ethanol (25 mL), followed by the above freshly prepared catalyst [which should be covered (50-100 mL) with ethanol to ca. 75% of the total flash volume. The hydrogenation was performed at an initial pressure of 60 psi at 50-55° C., and generally required 45-75 minutes. Nitrotirester 1 is quite insoluble in ethanol while amine 2 is soluble. External cooling may be necessary so that the temperature does not exceed 55° C. The catalyst was removed by filtration through a sintered glass funnel, then washed with ethanol (50-80 ml) (Catalyst Destruction). If there are traces of catalyst in the filtrate, filtration must be repeated. The solvent was removed in vacuo (0.1 mm) to yield an oil, which was transferred to a crystallizing dish and allowed to solidify in vacuo to give 41.5-44.1 g (89-93%) of 2 as a white crystalline mass, mp 51° C., lit. (Newkome et al., 1991) mp 51-52° C. ¹H NMR: δ 1.44 (s, CH₃, 27 H), 1.78 (m, CH₂, 12H); ¹³C NMR: δ 27.8 (CH₃), 29.8 (CH₂CO), 34.2 (CCH₂), 52.2 (CNH₂), 80.0 (CCH₃), 172.8 (CO₂); MS m/e 415.4 (M⁺+1, 20).

Amine 2 can be cyclized upon heating to 110° C. for 48 hours to yield (100%) lactam 3, mp 132-133° C., lit. (Young, 1993) mp 131-132° C. ¹H NMR: δ 1.44 (s, CH₃, 18 H), 1.83 (t, J=7.2 Hz, CH₂CO, 4H), 1.92 (t, J=8.0 Hz, CH₂CONH, 2H), 2.26 (t, J=7.2 Hz, CCH₂, 4H), 2.38 (5, J=8.0 Hz, CCH₂CH₂CH₂CONH, 2H), 6.92 (s, NH, 1H); ¹³C NMR: δ 27.9 (CH₃), 30.1 (CH₂O), 30.2, 30.25 [CH₂CH₂ (ring)], 34.6 (CH₂CH₂CO₂), 60.6 (HNC), 80.6 (CO₂C), 172.3 (CO₂), 177.2 (CONH); IR 1723, 1707 (C═O cm⁻¹. Anal. Calcd. for C₁₈H₃₁NO₅; C, 63.32; H, 9.15; N, 4.10. Found: C, 63.52; H, 9.25; N, 4.28.

The invention has been described in an illustrative manner, and it is to be understood that the terminology which has been used is intended to be in the nature of words of description rather than of limitation.

Obviously many modifications and variations of the present invention are possible in light of the above teachings. It is, therefore, to be understood that within the scope of the appended claims the invention may be practiced otherwise than as specifically described.

REFERENCES

-   1. Newkome, G. R.; Yao, Z.-q.; Baker, G. R.; Gupta, V. K. J. Org.     Chem. 1985, 50, 2003. -   2. Newkome, G. R.; Baker, G. R.; Saunders, M. J.; Russo, P. S.;     Gupta, V. K.; Yao, Z.-q. Y.; Miller, J. E.; Bouillion, K. J. Chem.     Soc., Chem. Commun. 1986, 752. -   3. Newkome, G. R.; Baker, G. R.; Aria, S.; Saunders, M. J.;     Russo, P. S.; Theriot, K. J.; Moorefield, C. N.; Rogers, L. E.;     Miller, J. E.; Lieux, T. R.; Murray, M. E.; Phillips, B.;     Pascal, L. J. Am. Chem. Soc. 1990, 112, 8458. -   4. Newkome, G. R.; Yao, Z.-q.; Baker, G. R.; Gupta, V. K.; Russo, P.     S.; Saunders, M. J.; J. Am. Chem. Soc. 1986, 108, 849. -   5. Newkome, G. R.; Hu, Y.; Saunders, M. J.; Fronczek, F. R.     Tetrahedron Lett. 1991, 32, 1133. -   6. Newkome, G. R.; Moorefield, C. N.; Baker, G. R.; Johnson, A. J.;     Behera, R. K. Angew. Chem. 1991, 103, 1205; Angew. Chem., Int. Ed.     Engl. 1991, 30, 1176. -   7. Newkome, G. R.; Moorefield, C. N.; Baker, G. R.; Saunders, M. J.;     Grossman, S. H. Angew. Chem. 1991, 103, 1207; Angew. Chem., Int. Ed.     Engl. 1991, 30, 1178. -   8. Newkome, G. R.; Lin, X. Macromolecules 1991, 24, 1443. -   9. Ingartinger, H.; Reimann, W. J. Org. Chem. 1988, 53, 3046. -   10. Bruson, H. A.; Riener, T. W. J. Amer. Chem. Soc. 1943, 65, 23. -   11. Gakenheimer, W. C.; Hartung, W. H. J. Org. Chem. 1944, 9, 85.     Noland, W. E.; Kneller, J. F.; Rice, D. E. Ibid. 1957, 22, 695.     Fanta, P. E.; Smat, R. J.; Piecz, L. F.; Clemens, L. Ibid. 1966,     31, 3113. Controulis, J.; Rebstock, M. C.; Crooks, H. M., Jr. J. Am.     Chem. Soc. 1949, 71, 2463. Wheatly, W. B. Ibid. 1954, 76, 2832.     Newman, M. S.; Edwards, W. M. Ibid. 1954, 76, 1840. Herz, W.;     Tocker, S. Ibid. 1955, 77, 3554. Baer, H. H.; Fischer, H. O. L.     Ibid. 1960, 82, 3709. -   12. Domingues, X. A.; Lopez, I. C.; Franco, R. J. Org. Chem. 1961,     26, 1625. -   13. Bodanszky, M.; Bodanszky, A. The Practice of Peptide Synthesis     in Reactivity and Structure Concepts in Organic Chemistry; 1984;     Vol. 21, p. 145. -   14. C. D. Weis and G. R. Newkome, Synthesis, 1053 (1995). -   15. J. K. Young, Ph. D. (USF) Dissertation, 1993. -   16. G. R. Newkome, R. K. Behera, C. N. Moorefield, G. R. Baker, J.     Org. Chem., 56, 7162 (1991). -   17. Catalyst destruction following the hydrogenation can be effected     by direct addition of the moist material to a 5%. aqueous HCl     solution. 

1. A method of forming an amine monomer of the formula

by the steps of reacting nitromethane and CH₂═CHCO₂-TBu by nucleophilic addition to form the triester nitrotrialkanoate of the formula

and reducing the nitrotrialkanoate to said amine monomer.
 2. A method as set forth in claim 1 wherein said reacting step is further defined as reacting said methyl nitromethane and CH₂═CHCO₂-TBu in the presence of dimethoxyethane and Triton-B at a temperature of about 70° to 80° C. for about one hour.
 3. A method as set forth in claim 1 wherein said reducing step is further defined as reducing the nitrotrialkanoate to the amine monomer with T-1 Raney nickel at a temperature of about 60° C.
 4. A method of forming a one-directional arborol of the formula

wherein R is t-Bu by the steps of treating adamantanecarbonyl chloride with di-tert-butyl 4-amino-[2-tert-butoxy-carbonyl)ethyl]-heptanedioate (amine monomer) to form a triester of the formula

wherein R is TBu and hydrolyzing said triester to a triacid, and peptide coupling amine monomers to each of the acid moieties of said triacid to form said arborol.
 5. A method as set forth in claim 4 wherein said treating step is conducted in the presence of NEt₃ and C₆H₆ at about 25° C. for about 20 hours.
 6. A method as set forth in claim 4 wherein said hydrolysis step is conducted in the presence of 96% HCO₂H at about 25° C. for about 20 hours.
 7. A method as set forth in claim 4 wherein said peptide coupling step is conducted in the presence of DCC, 1-hydroxybenzotriazole, and dimethylformamide at about 25° C. for about 24 hours.
 8. A method of forming a four-directional spherical dendritic macromolecule by the steps of treating an acid chloride of the formula

with an amine monomer, di-tert-butyl 4-amino-[2-(tert-butoxycarbonyl)ethyl]heptanedioate, to form a dodecaester of the formula

wherein R is t-Bu and adding additional layers of amine monomer by repeatedly hydrolyzing the ester, coupling the amine monomer to the acid moieties to form an additional tier of ester moieties and hydrolyzing to a corresponding acid.
 9. A compound of the formula

wherein R¹,R²,R³, and R⁴, are selected from the group consisting of hydrogen and cascade arborol branches, at least one of said R¹, R²,R³ and R⁴ being a cascade arborol branch.
 10. A compound of claim 9 of the formula


11. A compound as set forth in claim 9 of the formula


12. A compound of the formula

wherein R is selected from the group consisting essentially of NH₂ and NO₂.
 13. A compound of the formula


14. A compound of the formula


15. A method of forming an amine monomer of the formula

by the steps of (a) treating nitromethane with tert-butyl acrylate to form a nitrotriester of the formula

(b) recrystallizing the nitrotriester to remove impurities; and (c) hydrogenating the nitrotriester (II) to the aminotriester (I).
 16. A method as set forth in claim 15 wherein said treating step is further defined as treating the nitromethane with greater than three equivalents of the tert-butyl acrylate in dimethoxyethane.
 17. A method as set forth in claim 15 wherein said hydrogenating step is conducted using T-1 Raney Nickel at 45 to 55° C.
 18. A method as set forth in claim 15 wherein the hydrogenating step is followed by removing solvent in vacuo below 50° C. 19-22. (canceled) 